Shell Gadus S2 V20XKD/Shell Alvania Grease EP Artic Moly詳細說明 （瀏覽1455次）
Shell Gadus S2 V20XKD
High Performance Low Temperature Extreme Pressure
Grease with Solids
PRODUCT LINE
Shell Gadus S2 V20XKD Greases are premium quality, non-lead multi-purpose products based on
lithium soap. They were originally conceived and patented by Shell and have continuously been
improved over the years. Their multi-purpose nature allows for use in both heavy duty automotive and
industrial applications, thus reducing the need for specialty greases in specific applications. Shell
Gadus S2 V20XKD Grease is offered in NLGI grades 0 and contains 1% moly.
APPLICATIONS
Shell Gadus S2 V20XKD is specially designed for low temperature central system use down to -50°C.
PERFORMANCE BENEFITS
? Excellent Load Carrying Ability - Shell Gadus S2 V20XKD contains an extreme pressure
additive which imparts excellent load carrying properties -- translating into longer equipment
life.
? Anti-Rust Capability - The anti-rust additives promote excellent rust and corrosion protection
in wet conditions.
? Oxidation Stability - Longer lubricant life due to the oxidation inhibitors in Shell Gadus S2
V20XKD -- which means longer lubrication intervals and less grease usage.
? Resistance to Water Washout - Providing "stay-in" performance and extended relubrication
intervals.
? Wide Application Temperature Range - There is a grade available for applications from -
50°C to 80°C.
APPROVALS
Approved by CFIA (Canadian Food Inspection Agency) for industrial food plant use. Avoid food
contamination during application and storage.
Previous Name: Shell Alvania Grease EP Artic Moly
? Extreme Low Temperature
? Centralized Systems
? Lithium Technical Data Sheet
Shell Lubricants Page 2 of 2
18/04/2011
Shell Gadus Grease S2 V20XKD
NLGI Grade 0
Color Grey
Thickener Lithium
Estimated Operating Range, °C -50 to 80
Minimum Dispensing Temperature, -45
Dropping Point, °C 190
Mineral Oil Viscosity cSt at 40°C 20
Worked Penetration 60 strokes at 25°C 370
Worked Penetration 105 strokes at 25°C 400
Roll Stability (96hrs) -
4 Ball Wear Test mm 0.6
EP Tests
4-Ball, Load Wear Index
Timken Oil Load (kg)
40
18.2
Bomb Oxidation at 99°C
Pressure Drop at 100h, kPa 15
Bleed 24hrs @ 25°C, % wt 10
Corrosion Test,
48 hr. @ 52°C, Rating Pass
Mobility
@ -17.8 °C g/min
@ -40 °C g/min
-
2.1 |
|
|